Autolad3G
特点
● 兼容无铅制程
● 超低Z轴CTE：1.8%
● 高压耐CAF性能及优异的耐高低温循环性能
● 高耐热性能
应用领域
● 车载专用电子器件
● 线束箱
● 引擎及车身ECU
- 产品性能
- 产品证书
- 资料下载
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
| Tg | 2.4.24.4 | DMA | ℃ | 200 |
|
2.4.24.3 |
TMA | 180 | ||
| 2.4.25D |
DSC |
190 | ||
| Td | 2.4.24.6 | 5% wt. loss | ℃ | 408 |
|
T288 |
2.4.24.1 | TMA | min | >60 |
| T300 |
2.4.24.1 |
TMA |
min |
>60 |
|
Thermal Stress (Unetched/Etched) |
2.4.13.1 |
288℃, 20s solder dip |
- |
Pass/Pass |
| CTE (Z-axis) | 2.4.24 | Before Tg | ppm/℃ | 35 |
| After Tg | ppm/℃ | 180 | ||
| 50-260℃ | % | 1.8 | ||
| Dissipation Constant (10GHz) | 2.5.5.5 | C-24/23/50 | - | 4.0 |
|
Dissipation Factor (10GHz) |
2.5.5.5 |
C-24/23/50 |
- | 0.013 |
| Volume Resistivity | 2.5.17.1 | E-24/125 | MΩ.cm | 5.0×106 |
|
Surface Resistivity |
2.5.17.1 |
E-24/125 | MΩ | 2.0×108 |
| Arc Resistance | 2.5.1 | D-48/50+D-0.5/23 | s | 160 |
| Dielectric Breakdown | 2.5.6 | D-48/50+D-0.5/23 | kV | 45+kV NB |
| Peel Strength (1Oz) | 2.4.8 | 288℃/10s | N/mm | 1.3 [7.43] |
| Flexural Strength (LW/CW) | 2.4.4 | A | MPa | 560/450 |
| Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.13 |
|
Flammability |
UL94 |
C-48/23/50 |
Rating |
V-0 |
| CTI | IEC60112 | A | Rating | PLC3 |
Remarks:
Remark:
1. All the typical value is based onthe 1.6mm (8*7628) specimen. The Dk and Df value is based on 57% RC.
2. All the typical value listed above isfor your reference only, please turn to Shengyi Technology Co., Ltd fordetailed information, and all rights from this data sheet are reserved by ShengyiTechnology Co., Ltd.
Explanations:C=Humidity conditioning; D=Immersion conditioning in distilled water;E=Temperature conditioning.
The figures following the letter symbolsindicate with the first digit the duration of the preconditioning in hours,with the second digit the preconditioning temperature in ℃ and with the third digit the relative humidity.