Autolad2GH
特点
● CTI≥600V 以应对糟糕天气及为严格的线路设计提供足够的设计余量
● 高压耐CAF性能
● 优异的耐高低温循环性能
● 无卤素，不含锑和红磷
应用领域
● 大功率及高电压应用
● EV 车载电子部件
● 车载充电等
- 产品性能
- 产品证书
- 资料下载
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
| Tg | 2.4.24.4 | DMA | ℃ | 190 |
| 2.4.25D |
DSC |
175 | ||
| Td | 2.4.24.6 | 5% wt. loss | ℃ | 402 |
|
T288 |
2.4.24.1 | TMA | min | >60 |
| T260 |
2.4.24.1 |
TMA |
min |
>60 |
|
Thermal Stress |
2.4.13.1 |
288℃, solder dip |
- |
>100s No Delamination |
| CTE (Z-axis) | 2.4.24 | Before Tg | ppm/℃ | 35 |
| After Tg | ppm/℃ | 190 | ||
| 50-260℃ | % | 2.1 | ||
| Dissipation Constant (1GHz) | 2.5.5.9 | C-24/23/50 | - | 4.3 |
|
Dissipation Factor (1GHz) |
2.5.5.9 |
C-24/23/50 |
- | 0.015 |
| Volume Resistivity | 2.5.17.1 | C-96/35/90 | MΩ.cm | 4.83×107 |
|
Surface Resistivity |
2.5.17.1 |
C-96/35/90 | MΩ | 4.98×106 |
| Arc Resistance | 2.5.1 | D-48/50+D-0.5/23 | s | 130 |
| Dielectric Breakdown | 2.5.6 | D-48/50+D-0.5/23 | kV | 45+kV NB |
| Peel Strength (1Oz) | 2.4.8 | 288℃/10s | N/mm | 1.2 [6.86] |
| Flexural Strength (LW/CW) | 2.4.4 | A | MPa | 520/400 |
| Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.09 |
|
Flammability |
UL94 |
C-48/23/50 |
Rating |
V-0 |
| CTI | IEC60112 | A | Rating | PLC0(≥600V) |
Remarks:
Remark:
1. Specification sheet: IPC-4101/130, is for your reference only.
2. All the typical value is based on the 1.6mm (8X7628) specimen, “ * ” is based on the 1.0mm(9X2116) specimen.
3. In order to satisfy CTI≥600V, 2116(RC≥54%)，7628(RC≥45%) or above thickness prepreg is suggested to be used for outer prepreg layer.
4. All the typical value listed above is for your reference only, please turn to Shengyi Technology Co., Ltd for detailed information, and all rights from this data sheet are reserved by Shengyi Technology Co., Ltd.